LAP100.29D2 is suitable for production of high hardenability and high strength parts.
Diffusion-alloyed powders are based on the atomized iron powders and reduced sponge iron powders have been diffusion bonded with certain content Mo, Ni, Cu. This type of materials make it possible to produce the parts with good performance after heat treatment.
The high compressibility of atomized iron powder makes it a perfect choice for manufacturing pure iron or iron alloy parts with high tensile strength as well as high compressive strength. The Water atomized iron powder is mainly used in powder metallurgy for production of high strength machine parts. Water atomized iron powder may be mixed with graphite, nickel powder, copper powder and other metal powders to provide specific properties to the final product. It is also mixed with some lubricant such as zinc stearate before compaction.
Specification of Atomized iron powder LAP100.29D2
Chemical Properties(%) |
Unit |
Specification |
|
Min |
Max |
||
C |
% |
0.015 |
|
Si |
% |
0.05 |
|
Mn |
% |
0.15 |
|
P |
% |
0.015 |
|
S |
% |
0.015 |
|
Ni |
% |
3.80 |
4.20 |
Mo |
% |
0.50 |
0.70 |
Cu |
% |
1.60 |
1.90 |
HL |
% |
0.15 |
|
Physical Properties |
|||
Apparent density |
g/cm3 |
3.00 |
3.30 |
Flow rate |
s/50g |
30.00 |
|
Green density 600Mpa |
g/cm3 |
7.06 |
|
Particle size distribution(%) |
|||
180-212um |
% |
1 |
|
150-180um |
% |
10 |
|
45-150um |
% |
||
-45um |
% |
10 |
30 |
PROPERTIES
LAP100.29D2+0.3%C+0.6%Zn-st, condition: temperature1120℃, sintering time 30min.
PRODUCT PACKING
25kg/bag, 1000kg/bag, the package can be customized by buyer’s requirements.