Home > PRODUCT > Iron powder > atomized iron powder > iron powder for powder metallurgy
• Ni: 1.47 %
• Mo: 1.30 %
• Apparent density: 3.10 g/cm3
• Flow rate: 25.80 S/50g
• Green density 600Mpa: 7.00 g/cm3
• Particle size: 100 mesh
LAP100.29A4 is mainly used for sintered mechanical parts with good hardenability and high strength.
Pre-alloyed powders are water atomized steel powders with 0.85% Mo and 1.5% Mo often used as-sintered with additions of copper or nickel to make it possible for good surface hardening etc.
The high compressibility of atomized iron powder makes it a perfect choice for manufacturing pure iron or iron alloy parts with high tensile strength as well as high compressive strength. The Water atomized iron powder is mainly used in powder metallurgy for production of high strength machine parts. Water atomized iron powder may be mixed with graphite, nickel powder, copper powder and other metal powders to provide specific properties to the final product. It is also mixed with some lubricant such as zinc stearate before compaction.
Specification of Atomized iron powder LAP100.29A4
| Chemical Properties（%） | Unit | Specification | |
| Min | Max | ||
| C | % | 0.01 | |
| Si | % | 0.05 | |
| Mn | % | 0.35 | 0.55 |
| P | % | 0.020 | |
| S | % | 0.015 | |
| Ni | % | 1.30 | 1.55 |
| Mo | % | 1.15 | 1.40 |
| HL | % | 0.25 | |
| Physical Properties | |||
| Apparent density | g/cm3 | 2.90 | 3.20 |
| Flow rate | s/50g | 28.00 | |
| Green density 600Mpa | g/cm3 | 6.65 | |
| Particle size distribution（%） | |||
| 180-212um | % | 1 | |
| 150-180um | % | 10 | |
| 45-150um | % | ||
| -45um | % | 10 | 30 |
PROPERTIES
LAP100.29A1+0.80%C +0.80%Zn-st, condition: temperature1125℃, sintering time 30min.
PRODUCT PACKING
25kg/bag, 1000kg/bag, the package can be customized by buyer’s requirements.