Pure atomized iron powder LAP100.29H

LAP100.29H is widely used for the production of sintered metal parts with density above 6.8g/cm3 and PM forged parts.

Water atomized iron powder has irregularly shaped and high apparent density 2.90-3.10g/cm³，the particles is about 150um, the green density can reach 7.2 g/cm.

The high compressibility of atomized iron powder makes it a perfect choice for manufacturing pure iron or iron alloy parts with high tensile strength as well as high compressive strength. The Water atomized iron powder is mainly used in powder metallurgy for production of high strength machine parts. Water atomized iron powder may be mixed with graphite, nickel powder, copper powder and other metal powders to provide specific properties to the final product. It is also mixed with some lubricant such as zinc stearate before compaction.

PROPERTIES
Composition: Fe-1.5%; Cu-0.6%; Gr-0.8ZnSt. Sintering condition: 1120℃ × 30 min, cracked ammonia.

PRODUCT PACKING
25kg/bag, 1000kg/bag, the package can be customized by buyer’s requirements.